Preparation of Highly Dispersed Core/Shell-type Titania Nanocapsules Containing a Single Ag Nanoparticle
Citations Over TimeTop 10% of 2006 papers
Abstract
Core/shell-type titania nanocapsules containing a single Ag nanoparticle were prepared. Ag nanoparticles were prepared using the reduction of silver nitrate with hydrazine in the presence of cetyltrimethylammonium bromide (CTAB) as protective agent. The sol-gel reaction of titanium tetraisopropoxide (TTIP) was used to prepare core/shell-type titania nanocapsules with CTAB-coated Ag nanoparticles as the core. TEM observations revealed that the size of the core (Ag particle) and the thickness of the shell (titania) of the core/shell particles obtained are about 10 nm and 5-10 nm, respectively. In addition, the nanocapsules were found to be dispersed in the medium as individual particles without aggregation. Moreover, titania coating caused the surface plasmon absorption of Ag nanoparticles to shift toward the longer wavelength side.
Related Papers
- → Safety profile and cellular uptake of biotemplated nanocapsules with nanometre-thin walls(2011)8 cited
- → Organic Nanocapsules(2008)3 cited
- Properties of Aroma Sustained-release Cotton Fabric with Rose Fragrance Nanocapsule(2011)
- Development and Properties of Temperature-sensitive Poly(N-isopropylacrylamide) Nanocapsules(2012)
- Magnetic and Microwave-absorption Properties of Graphite-coated （Fe, Ni） Nanocapsules(2011)