Competition as a Design Concept: Polymorphism in Self-Assembled Monolayers of Biphenyl-Based Thiols

Citations Over TimeTop 10% of 2006 papers

Abstract

Self-assembled monolayers (SAMs) of two omega-(4'-methylbiphenyl-4-yl)alkanethiols (CH(3)(C(6)H(4))(2)(CH(2))(n)SH, BPn, n = 4, 6) on Au(111) substrates, prepared from solution at room temperature and subsequently annealed at temperatures up to 493 K under a nitrogen atmosphere, were studied using scanning tunneling microscopy (STM), high-resolution X-ray photoelectron spectroscopy (HRXPS), and near-edge X-ray absorption fine structure spectroscopy (NEXAFS). In striking contrast to BPn SAMs with n = odd, for which only one phase is observed, the even-numbered BPn SAMs exhibit polymorphism. Irreversible phase transitions occur which involve three phases differing substantially in density and stability. Upon annealing, BP4 and BP6 transform into a beta-phase, which is characterized by an exceptionally high structural quality with virtually defect-free domains exceeding 500 nm in diameter. Exchange experiments, monitored by contact angle measurement, reveal that the beta-phase exhibits a dramatically improved stability. The fundamental differences in the phase behavior of even- and odd-numbered BPn SAMs are discussed in terms of two design strategies based on cooperative and competitive effects.

Related Papers

• → Structural ordering of ω-ferrocenylalkanethiol monolayers on Au(111) studied by scanning tunneling microscopy(2009)17 cited
• → Mixed SAMs of backbone-functionalized tribenzotriquinacenes and alkanethiols: Synthesis, preparation and STM-investigations(2015)10 cited
• → Scanning tunneling microscopy of locally derivatized self-assembled organic monolayers(2003)3 cited
• CYCLIC VOLTAMMETRY STUDY OF SELF-ASSEMBLED LAYER ON SILVER(2006)
• Formation process and topography characteristics of OTS self-assembled monolayers(2002)