High-Capacity Hydrogen and Nitric Oxide Adsorption and Storage in a Metal−Organic Framework
Citations Over TimeTop 1% of 2007 papers
Abstract
Gas adsorption experiments have been carried out on a copper benzene tricarboxylate metal-organic framework material, HKUST-1. Hydrogen adsorption at 1 and 10 bar (both 77 K) gives an adsorption capacity of 11.16 mmol H2 per g of HKUST-1 (22.7 mg g(-)1, 2.27 wt %) at 1 bar and 18 mmol per g (36.28 mg g(-)1, 3.6 wt %) at 10 bar. Adsorption of D2 at 1 bar (77 K) is between 1.09 (at 1 bar) and 1.20(at <100 mbar) times the H2 values depending on the pressure, agreeing with the theoretical expectations. Gravimetric adsorption measurements of NO on HKUST-1 at 196 K (1 bar) gives a large adsorption capacity of approximately 9 mmol g(-1), which is significantly greater than any other adsorption capacity reported on a porous solid. At 298 K the adsorption capacity at 1 bar is just over 3 mmol g(-1). Infra red experiments show that the NO binds to the empty copper metal sites in HKUST-1. Chemiluminescence and platelet aggregometry experiments indicate that the amount of NO recovered on exposure of the resulting complex to water is enough to be biologically active, completely inhibiting platelet aggregation in platelet rich plasma.
Related Papers
- → Comparative analysis of the efficiencies of hydrogen storage systems utilising solid state H storage materials(2014)85 cited
- → A comparison of hydrogen storage in activated carbons and a metal–organic framework (MOF-5)(2010)73 cited
- → New isoreticular metal-organic framework materials for high hydrogen storage capacity(2005)67 cited
- → First principle study of hydrogen storage in doubly substituted Mg based hydrides Mg5MH12 (M = B, Li) and Mg4BLiH12(2016)42 cited
- → Stability and Hydrogen Storage Properties of Mx-B6H6 Complexes (M = Y–Mo, Ru–Ag, x = 1–2)(2021)5 cited