Cross-Linking of Cationic Block Copolymer Micelles by Silica Deposition

Citations Over TimeTop 1% of 2007 papers

Abstract

Diblock copolymer micelles comprising cationic poly(2-(dimethylamino)ethyl methacrylate) (PDMA) coronas and hydrophobic poly(2-(diisopropylamino)ethyl methacrylate) (PDPA) cores are used as nanosized templates for the deposition of silica from aqueous solution at pH 7.2 and 20 degrees C. Both noncross-linked and shell cross-linked (SCL) micelles can be coated with silica without loss of colloid stability. Under optimized conditions, the silica deposition is confined to the partially quaternized cationic PDMA chains, leading to hybrid copolymer-silica particles of around 35 nm diameter with well-defined core-shell morphologies. 1H NMR studies confirmed that the PDPA cores of these copolymer-silica particles became protonated at low pH and deprotonated at high pH, which suggests possible encapsulation and controlled release applications. Moreover, in situ silica deposition effectively stabilizes the PDPA-PDMA micelles, which remain intact on lowering the solution pH (whereas the original noncross-linked PDPA-PDMA micelles dissociate in acidic solution). This suggests a convenient route to silica-stabilized SCL micelles under mild conditions.

Related Papers

• → Are the Interfacial Basicities of Aqueous Cationic Micelles and Cationic Reverse Microemulsions Different by Orders of Magnitude?(1999)26 cited
• → Cationic Copolymerization of Tetrahydrofuran with ε-Caprolactone(1972)13 cited
• → Cationic copolymerization behavior of epoxide and 3-isochromanone(2013)7 cited
• → The copolymerization of methacrylaldehyde with hydrophilic monomers(1980)5 cited
• → Cationic Ring-opening Polymerization: Copolymerization(1989)