Methodology for Synthesizing Crystalline Metallosilicates with Expanded Pore Windows Through Molecular Alkoxysilylation of Zeolitic Lamellar Precursors

Citations Over TimeTop 10% of 2008 papers

Abstract

Postalkoxysilylation with diethoxydimethylsilane has been carried out on the zeolitic lamellar precursors of various topologies such as MWW, FER, CDO and MCM-47 aiming to construct new crystalline structures with expanded pore apertures between the layers. The silylation process and the crystalline and pore structures of the resulting materials have been investigated with the techniques of XRD, IR, (13)C and (29)Si MAS NMR, ICP, SEM, HRTEM, elemental analyses, and N 2 adsorption. In contrast to forming known three-dimensional zeolite structures after direct calcination of the lamellar precursors, the silylation led to new crystalline structures with opener pores, as evidenced by the shift of layer-related diffractions to the lower-angle region in XRD patterns and the enlarged interlayer pores found by HRTEM images. After optimizing the treatment conditions, particularly the amount of silane agent, a maximum and homogeneous silylation was realized, which guaranteed the phase purity in interlayer expanded zeolites. The expanded structures were well preserved after calcination at 823 K or reflux in water for 1 to 2 weeks, indicating a high thermal stability and also a hydrothermal stability. The interlayer expanded zeolites prepared from the metallosilicate precursors of MWW topology exhibited higher catalytic activities in the redox and solid acid-catalyzed reactions of bulky molecules than that of their counterparts with conventional MWW topology.

Related Papers

• → Synthesis and Reactivity of Silyl Vinylketenes: A Formal Interrupted Dötz Benzannulation with Unexpected Silyl Migration(2001)38 cited
• → Facile synthesis of silyl allenol ethers and β-silyl enones through reductive silylation of benzoylacetylenes(2022)2 cited
• Polysulfone으로 제올라이트 A를 고정화한 방사성 물질제거용 PS-zeolite 비드 제조(2015)
• The effect of calcination conditions on the photocatalytic performance of CaTiO_3(2007)
• 쳔연 Zeolite ( 제올라이트 ) 를 이용한 중금속 흡착제의 개발(1991)