Yb@C2n (n = 40, 41, 42): New Fullerene Allotropes with Unexplored Electrochemical Properties
Citations Over TimeTop 10% of 2010 papers
Abstract
A series of(13)C-enriched monoytterbium endohedral metallofullerenes (EMFs)-Yb@C(2n) (n = 40, 41, 42)-was synthesized and isolated. Their cage structures were systematically determined for the first time using computational and experimental (13)C NMR studies. The results revealed that all isomers adopt cage structures conforming to the isolated pentagon rule. In detail, Yb@C(80) possesses the C(2v)(3) cage; Yb@C(82)(I, II, III) bear C(s)(6), C(2)(5), and C(2v)(9) cages, respectively; and Yb@C(84)(II, III, IV) have C(2)(13), C(1)(12), and C(2)(11) cage structures, respectively. This is the first report describing C(2)(13)-C(84) and C(1)(12)-C(84) cage structures. It is noteworthy that the cage structures found for mono-EMFs generally differ from either the corresponding empty fullerenes or the related EMFs encapsulating more than one metal atom, indicating that the metal atom inside the fullerene cage plays an important role in determining the EMF structure. On the basis of the fact that the structure of Yb@C(2)(13)-C(84) resembles that of Yb@C(2)(5)-C(82), a metal-templated growth process was proposed as a kinetic factor controlling EMF formation. Furthermore, previous electrochemical studies of divalent EMFs have failed to observe their oxidation potentials, which have raised the assumption that such species are large-bandgap molecules. This study revealed that all isomers of Yb@C(2n) (n = 40, 41, 42) display one or two reversible oxidation steps together with four reversible reduction processes in 1,2-dichlorobenzene, even at a low scan rate (20 mV/s), which enables estimation of their electrochemical bandgaps (DeltaE = (ox)E(1)-(red)E(1)). The results show a DeltaE value of 0.88-1.41 V for Yb@C(2n) (2n = 40, 41, 42), which is much larger than the values of trivalent mono-EMFs (DeltaE < 0.5 V), but generally smaller than those of metal nitride cluster EMFs (1.4 V < DeltaE < 2.1 V). Results further demonstrated that the DeltaE values correlate reasonably with their relative abundances.
Related Papers
- → Physical and chemical evidence for metallofullerenes with metal atoms as part of the cage(1994)129 cited
- → Water Molecule and Atoms Inside C60 Fullerene(2020)2 cited
- → Endohedral fullerenes with lower carbon cage sizes(1999)
- → Reactor R&D: Effect of Plasma Additives on Endohedral Metallofullerene and Empty-Cage Fullerenes(2016)
- Reactor R&D: Synthesis and Optimization of Metallic Nitride Fullerenes and the Introduction of Two New Classes of Endohedral Metallofullerenes, Metallic Nitride Azafullerenes and Oxo-Metallic Fullerenes(2009)