Mesoporous Silica-Coated Hollow Manganese Oxide Nanoparticles as Positive T1 Contrast Agents for Labeling and MRI Tracking of Adipose-Derived Mesenchymal Stem Cells
Citations Over TimeTop 1% of 2011 papers
Abstract
Mesoporous silica-coated hollow manganese oxide (HIVInO@ mSiO(2)) nanoparticles were developed as a novel T-1 magnetic resonance imaging (MRI) contrast agent. We hypothesized that the mesoporous structure of the nanopartide shell enables optimal access of water molecules to the magnetic core, and consequently, an effective longitudinal (R-1) relaxation enhancement of water protons, which value was measured to be 0.99 (mM(-1) s(-1)) at 11.7 T. Adipose-derived mesenchymal stem cells (MSCs) were efficiently labeled using electroporation, with much shorter T-1 values as compared to direct incubation without electroporation, which was also evidenced by signal enhancement on T-1-weighted MR images in vitro. Intracranial grafting of HMnO@mSiO(2)-labeled MSCs enabled serial MR monitoring of cell transplants over 14 days. These novel nanopartides may extend the arsenal of currently available nanoparticie MR contrast agents by providing positive contrast on T-1-weighted images at high magnetic field strengths.
Related Papers
- → The gadolinium complexes with polyoxometalates as potential MRI contrast agents(2007)53 cited
- → Design and synthesis of novel DOTA(Gd3+)–polymer conjugates as potential MRI contrast agents(2011)31 cited
- → A self-assembly heterotrinuclear gadolinium(III)–iron(II) complex as a MRI contrast agent(2011)13 cited
- → Gadolinium-Mesoporous Silica as a Potential Magnetic Resonance Imaging Contrast Agents(2018)3 cited
- Relaxivities of Gadolinium Heteropoly Complexes in Aqueous Solution for MRI Contrast Agent(2000)