Synthesis of Pd−Pt Bimetallic Nanocrystals with a Concave Structure through a Bromide-Induced Galvanic Replacement Reaction

Citations Over TimeTop 1% of 2011 papers

Abstract

This article describes a systematic study of the galvanic replacement reaction between PtCl(6)(2-) ions and Pd nanocrystals with different shapes, including cubes, cuboctahedrons, and octahedrons. It was found that Br(-) ions played an important role in initiating, facilitating, and directing the replacement reaction. The presence of Br(-) ions led to the selective initiation of galvanic replacement from the {100} facets of Pd nanocrystals, likely due to the preferential adsorption of Br(-) ions on this crystallographic plane. The site-selective galvanic replacement resulted in the formation of Pd-Pt bimetallic nanocrystals with a concave structure owing to simultaneous dissolution of Pd atoms from the {100} facets and deposition of the resultant Pt atoms on the {111} facets. The Pd-Pt concave nanocubes with different weight percentages of Pt at 3.4, 10.4, 19.9, and 34.4 were also evaluated as electrocatalysts for the oxygen reduction reaction (ORR). Significantly, the sample with a 3.4 wt.% of Pt exhibited the largest specific electrochemical surface area and was found to be four times as active as the commercial Pt/C catalyst for the ORR in terms of equivalent Pt mass.

Related Papers

• → Bimetallic Sites for Catalysis: From Binuclear Metal Sites to Bimetallic Nanoclusters and Nanoparticles(2023)549 cited
• → Defects engineering of bimetallic Ni-based catalysts for electrochemical energy conversion(2020)60 cited
• → Chemical Preparation of Supported Bimetallic Catalysts. Gold-Based Bimetallic, a Case Study(2016)46 cited
• → Facile synthesis of bimetallic Ni-Cu nanoparticles using liquid phase plasma method(2016)26 cited
• → A new type of catalysts: catalysts of singly dispersed bimetallic sites(2023)12 cited