Ultrasmall Near-Infrared Ag2Se Quantum Dots with Tunable Fluorescence for in Vivo Imaging
Citations Over TimeTop 1% of 2011 papers
Abstract
A strategy is presented that involes coupling Na(2)SeO(3) reduction with the binding of silver ions and alanine in a quasi-biosystem to obtain ultrasmall, near-infrared Ag(2)Se quantum dots (QDs) with tunable fluorescence at 90 °C in aqueous solution. This strategy avoids high temperatures, high pressures, and organic solvents so that water-dispersible sub-3 nm Ag(2)Se QDs can be directly obtained. The photoluminescence of the Ag(2)Se QDs was size-dependent over a wavelength range from 700 to 820 nm, corresponding to sizes from 1.5 ± 0.4 to 2.4 ± 0.5 nm, with good monodispersity. The Ag(2)Se QDs are less cytotoxic than other nanomaterials used for similar applications. Furthermore, the NIR fluorescence of the Ag(2)Se QDs could penetrate through the abdominal cavity of a living nude mouse and could be detected on its back side, demonstrating the potential applications of these less toxic NIR Ag(2)Se QDs in bioimaging.
Related Papers
- → La2MgTiO6:Bi3+/Mn4+ photoluminescence materials: Molten salt preparation, Bi3+ → Mn4+ energy transfer and thermostability(2020)21 cited
- → Photoluminescence of porous Si, oxidized then deoxidized chemically(1992)109 cited
- → Study of delocalized and localized states in ZnSeO layers with photoluminescence, micro-photoluminescence, and time-resolved photoluminescence(2019)7 cited
- → Excitons imaging in hybrid organic-inorganic films(2012)3 cited
- Photoluminescence excitation spectroscopy yields bandgap of Ga_5In_5P containing relatively ordered domains(1993)