Toward Inexpensive Superhard Materials: Tungsten Tetraboride-Based Solid Solutions
Citations Over TimeTop 10% of 2012 papers
Abstract
To enhance the hardness of tungsten tetraboride (WB(4)), a notable lower cost member of the late transition-metal borides, we have synthesized and characterized solid solutions of this material with tantalum (Ta), manganese (Mn), and chromium (Cr). Various concentrations of these transition-metal elements, ranging from 0.0 to 50.0 at. %, on a metals basis, were made. Arc melting was used to synthesize these refractory compounds from the pure elements. Elemental and phase purity of the samples were examined using energy-dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD), and microindentation was utilized to measure the Vickers hardness under applied loads of 0.49-4.9 N. XRD results indicate that the solubility limit is below 10 at. % for Cr and below 20 at. % for Mn, while Ta is soluble in WB(4) above 20 at. %. Optimized Vickers hardness values of 52.8 ± 2.2, 53.7 ± 1.8, and 53.5 ± 1.9 GPa were achieved, under an applied load of 0.49 N, when ~2.0, 4.0, and 10.0 at. % Ta, Mn, and Cr were added to WB(4) on a metals basis, respectively. Motivated by these results, ternary solid solutions of WB(4) were produced, keeping the concentration of Ta in WB(4) fixed at 2.0 at. % and varying the concentration of Mn or Cr. This led to hardness values of 55.8 ± 2.3 and 57.3 ± 1.9 GPa (under a load of 0.49 N) for the combinations W(0.94)Ta(0.02)Mn(0.04)B(4) and W(0.93)Ta(0.02)Cr(0.05)B(4), respectively. In situ high-pressure XRD measurements collected up to ~65 GPa generated a bulk modulus of 335 ± 3 GPa for the hardest WB(4) solid solution, W(0.93)Ta(0.02)Cr(0.05)B(4), and showed suppression of a pressure-induced phase transition previously observed in pure WB(4).
Related Papers
- A GEOMETRIC MEAN IN THE FURUTA INEQUALITY(2002)
- Susquehanna Chorale Spring Concert "Roots and Wings"(2017)
- Коммуникaтивно- прaгмaтический aнaлиз дипломaтических бумaг (нa основе вербaльных нот)(2018)
- → ФОРМИРОВAНИЕ ГОТОВНОСТИ БУДУЩИХ ПЕДAГОГОВ К ОРГAНИЗAЦИИ РAБОТЫ ПО РAЗВИТИЮ ВAЛЕОЛОГИЧЕСКОЙ КУЛЬТУРЫ ШКОЛЬНИКОВ(2023)