Experimental and Theoretical Investigation of Molybdenum Carbide and Nitride as Catalysts for Ammonia Decomposition

Citations Over TimeTop 1% of 2013 papers

Abstract

Constant CO(x)-free H2 production from the catalytic decomposition of ammonia could be achieved over a high-surface-area molybdenum carbide catalyst prepared by a temperature-programmed reduction-carburization method. The fresh and used catalyst was characterized by N2 adsorption/desorption, powder X-ray diffraction, scanning and transmission electron microscopy, and electron energy-loss spectroscopy at different stages. Observed deactivation (in the first 15 h) of the high-surface-area carbide during the reaction was ascribed to considerable reduction of the specific surface area due to nitridation of the carbide under the reaction conditions. Theoretical calculations confirm that the N atoms tend to occupy subsurface sites, leading to the formation of nitride under an NH3 atmosphere. The relatively high rate of reaction (30 mmol/((g of cat.) min)) observed for the catalytic decomposition of NH3 is ascribed to highly energetic sites (twin boundaries, stacking faults, steps, and defects) which are observed in both the molybdenum carbide and nitride samples. The prevalence of such sites in the as-synthesized material results in a much higher H2 production rate in comparison with that for previously reported Mo-based catalysts.

Related Papers

• → A Parallel Colorimetric Method for the Rapid Discovery and Optimization of Heterogeneous Hydrodesulfurization Catalysts(2003)16 cited
• → Chemical and Electrochemical Methods of Separating the Carbides MeC and the Carbonitrides Me(C,N) of Group IV and V Metals(1972)2 cited
• → Catalytic activity of NiMo/TiO2−Al2O3 systems in thiophene hydrodesulfurization(1995)11 cited
• → In Situ Radioisotopic Study of the Active Sites of Sulfide CoMo Catalysts and the Mechanism of Thiophene Hydrodesulfurization(2003)10 cited
• Study on impact of H_2S on diesel hydrodesulfurization(2012)