High-Performance Tellurium-Free Thermoelectrics: All-Scale Hierarchical Structuring of p-Type PbSe–MSe Systems (M = Ca, Sr, Ba)
Citations Over TimeTop 10% of 2013 papers
Abstract
We present a systematic study of the characterization and thermoelectric properties of nanostructured Na-doped PbSe embedded with 1-4% MSe (M = Ca, Sr, Ba) phases as endotaxial inclusions. The samples were powder-processed by the spark plasma sintering technique, which introduces mesoscale-structured grains. The hierarchical architectures on the atomic scale (Na and M solid solution), nanoscale (MSe nanoprecipitates), and mesoscale (grains) were confirmed by transmission electron microscopy. These structures produce a great reduction in the lattice thermal conductivity relative to pristine PbSe without appreciably affecting the power factor. The lattice thermal conductivity can be reduced by up to ∼29% when the second phase is added. The highest ZT value achieved was ∼1.3 at 923 K for both 2% SrSe-and 3% BaSe-containing samples, while the sample containing 4% CaSe showed a ZT value of ∼1.2 at 923 K. The optimal samples have hole carrier concentration of 1-2 × 10(20) cm(-3). We attribute the high ZT values to the combination of broad-based phonon scattering on multiple length scales and favorable charge transport through coherent interfaces between the PbSe matrix and MSe.
Related Papers
- → High-performance SnSe thermoelectric materials: Progress and future challenge(2018)568 cited
- → Optimized Strategies for Advancing n-Type PbTe Thermoelectrics: A Review(2020)95 cited
- → Strategies and challenges of high-pressure methods applied to thermoelectric materials(2019)64 cited
- → Comparison of the electronic and thermoelectric properties of three layered phases Bi2Te3, PbBi2Te4 and PbBi4Te7: LEGO thermoelectrics(2018)20 cited
- → Single‐Molecule Thermoelectric Devices(2022)