Size Specifically High Activity of Ru Nanoparticles for Hydrogen Oxidation Reaction in Alkaline Electrolyte
Citations Over TimeTop 10% of 2013 papers
Abstract
The hydrogen oxidation reaction (HOR) in alkaline electrolyte was conducted on carbon-supported Ru nanoparticles (Ru/C) of which size was controlled in the range from approximately 2 to 7 nm. The HOR activity of Ru/C normalized by the metal surface area showed volcano shaped dependence on the particle size with a maximum activity at approximately 3 nm. The HOR activity of approximately 3 nm Ru/C was higher than commercially available Pt nanoparticles (ca. 2 nm) supported on carbon. The structural analysis of Ru/C using Cs-corrected scanning transmission electron microscopy with atomic resolution revealed the unique structural change of Ru/C different from Pt/C: Ru nanoparticle structure changed from amorphous-like structure below 3 nm to metal nanocrystallite with roughened surface at approximately 3 nm and then to that with well-defined facets above 3 nm, although Pt/C kept well-defined facets even at approximately 2 nm. It is proposed that the generation of unique structure observed on approximately 3 nm Ru nanoparticles, that is, long bridged coordinatively unsaturated Ru metal surface atoms on its nanocrystallite, is a key to achieve high HOR activity.
Related Papers
- → Extractive Separation and Spectrophotometric Determination of Traces of Ruthenium from Mixtures Containing Excess Platinum Group Metals(2009)7 cited
- → Ligand control of metal oxidation states. Synthesis, characterization and cyclic voltammetric studies of a group of ruthenium phenolates(1996)18 cited
- THE FEATURES OF PROTEIN BINDING BY RUTHENIUM COMPLEXES: DOCKING, FORCE FIELD AND QM/MM STUDIES(2013)
- → Phosphorogenic and spontaneous formation of tris(bipyridine)ruthenium in peptide scaffolds(2019)1 cited
- → ChemInform Abstract: Synthesis, Reactivities, and Structural Studies on High‐Valent Ruthenium Oxo Complexes. Ruthenium(IV), Ruthenium(V), and Ruthenium(VI) Oxo Complexes of Tertiary Amine Ligands.(1987)