Structural Complexity in Metal–Organic Frameworks: Simultaneous Modification of Open Metal Sites and Hierarchical Porosity by Systematic Doping with Defective Linkers

Citations Over TimeTop 10% of 2014 papers

Abstract

A series of defect-engineered metal-organic frameworks (DEMOFs) derived from parent microporous MOFs was obtained by systematic doping with defective linkers during synthesis, leading to the simultaneous and controllable modification of coordinatively unsaturated metal sites (CUS) and introduction of functionalized mesopores. These materials were investigated via temperature-dependent adsorption/desorption of CO monitored by FTIR spectroscopy under ultra-high-vacuum conditions. Accurate structural models for the generated point defects at CUS were deduced by matching experimental data with theoretical simulation. The results reveal multivariate diversity of electronic and steric properties at CUS, demonstrating the MOF defect structure modulation at two length scales in a single step to overcome restricted active site specificity and confined coordination space at CUS. Moreover, the DEMOFs exhibit promising modified physical properties, including band gap, magnetism, and porosity, with hierarchical micro/mesopore structures correlated with the nature and the degree of defective linker incorporation into the framework.

Related Papers

• → Specific Surface Area Determination for Microporous/Mesoporous Materials: The Case of Mesoporous FAU-Y Zeolites(2018)112 cited
• → Mesoporous and microporous carbons from one-pot hydrothermal products for supercapacitor electrodes: effects of porous structures and surface functionality(2023)8 cited
• → Synthesis strategies for the preparation of mixed micro-mesoporous materials(2008)4 cited
• → The synthesis of mesoporous materials with semicrystalline microporous walls(2003)3 cited
• Synthesis,Characterization and Catalytic Properties of Mesoporous Materials with Loading of TS-1 Precursors(2004)