Comparative Study of Hydrogen Sulfide Adsorption in the MIL-53(Al, Cr, Fe), MIL-47(V), MIL-100(Cr), and MIL-101(Cr) Metal−Organic Frameworks at Room Temperature
Journal of the American Chemical Society2009Vol. 131(25), pp. 8775–8777
Citations Over TimeTop 1% of 2009 papers
Lomig Hamon, Christian Serre, Thomas Devic, Thierry Loiseau, Franck Millange, Gérard Férey, Guy De Weireld
Abstract
Hydrogen sulfide gravimetric isotherm adsorption measurements were carried out on MIL-53(Al, Cr, Fe), MIL-47(V), MIL-100(Cr), and MIL-101(Cr) metal-organic frameworks (MOFs). A two-step adsorption mechanism related to a breathing effect was observed for MIL-53 terephthalate-based MOFs. Methane adsorption measurements highlighted the regenerability of MIL-53(Al, Cr) and MIL-47(V) MOFs after H(2)S treatment, whereas MIL-100 and MIL-101 CH(4) adsorption capacities were significantly decreased.
Related Papers
- → Adsorption and reaction behavior for the simultaneous adsorption of NO–NO2 and SO2 on activated carbon impregnated with KOH(2003)80 cited
- → Adsorption of methylene blue and bright blue dyes on bayleaf capertree pods powder: Understanding the adsorption mechanism by a theoretical study(2021)43 cited
- The study of Zn~(2+) and Cd~(2+) adsorption on activated carbon modified with KMnO_4(2010)
- [Adsorption properties of dye compounds on the sediments in Qinghe].(2002)
- → Preparation of corn stalk adsorbent and its adsorption performance for Pb2+ in aqueous solution(2022)