Solar Water Oxidation by Composite Catalyst/α-Fe₂O₃ Photoanodes

Citations Over TimeTop 1% of 2009 papers

Abstract

Electrodeposition of an amorphous cobalt catalyst layer over a high-surface-area alpha-Fe(2)O(3) photoanode causes a more than 350 mV cathodic shift in the onset potential for photoelectrochemical water oxidation using this anode and simulated solar irradiation. The catalyst layer is shown to deposit conformally onto the mesostructured alpha-Fe(2)O(3), leading to a large contact area at the interface between the two halves of the composite photoanode. Photoelectrochemical measurements show that the photocurrent generated from this composite photoanode still derives from alpha-Fe(2)O(3) excitation but is now accessible at an external bias several hundred millivolts below what is typically required for alpha-Fe(2)O(3) photoanodes alone, indicating a reduced external bias would be needed to drive overall water splitting. These results demonstrate modification of this prototypical photoanode material with a conformal layer of a competent electrocatalyst to separate the tasks of photon absorption and redox catalysis, a strategy that may have important and general ramifications for solar photoelectrochemical hydrogen generation.

Related Papers

• → Amorphous Catalysts and Electrochemical Water Splitting: An Untold Story of Harmony(2019)656 cited
• → Fabrication of an Efficient BaTaO₂N Photoanode Harvesting a Wide Range of Visible Light for Water Splitting(2013)224 cited
• → Hierarchically branched Fe₂O₃@TiO₂nanorod arrays for photoelectrochemical water splitting: facile synthesis and enhanced photoelectrochemical performance(2016)92 cited
• → Bifunctional electrocatalytic water splitting augmented by cobalt-nickel-ferrite NPs-supported fluoride-free MXene as a novel electrocatalyst(2023)62 cited
• → Reply to Comment on “Commercially Available WO₃ Nanopowders for Photoelectrochemical Water Splitting: Photocurrent versus Oxygen Evolution”(2017)