Observation of Photovoltaic Action from Photoacid-Modified Nafion Due to Light-Driven Ion Transport

Citations Over TimeTop 10% of 2017 papers

Abstract

Replacing passive ion-exchange membranes, like Nafion, with membranes that use light to drive ion transport would allow membranes in photoelectrochemical technologies to serve in an active role. Toward this, we modified perfluorosulfonic acid ionomer membranes with organic pyrenol-based photoacid dyes to sensitize the membranes to visible light and initiate proton transport. Covalent modification of the membranes was achieved by reacting Nafion sulfonyl fluoride poly(perfluorosulfonyl fluoride) membranes with the photoacid 8-hydroxypyrene-1,3,6-tris(2-aminoethylsulfonamide). The modified membranes were strongly colored and maintained a high selectivity for cations over anions. Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and ion-exchange measurements together provided strong evidence of covalent bond formation between the photoacids and the polymer membranes. Visible-light illumination of the photoacid-modified membranes resulted in a maximum power-producing ionic photoresponse of ∼100 μA/cm2 and ∼1 mV under 40 Suns equivalent excitation with 405 nm light. In comparison, membranes that did not contain photoacids and instead contained ionically associated RuII-polypyridyl coordination compound dyes, which are not photoacids, exhibited little-to-no photoeffects (∼1 μA/cm2). These disparate photocurrents, yet similar yields for nonradiative excited-state decay from the photoacids and the RuII dyes, suggest temperature gradients were not likely the cause of the observed photovoltaic action from photoacid-modified membranes. Moreover, spectral response measurements supported that light absorption by the covalently bound photoacids was required in order to observe photoeffects. These results represent the first demonstration of photovoltaic action from an ion-exchange membrane and offer promise for supplementing the power demands of electrochemical processes with renewable sunlight-driven ion transport.

Related Papers

• → Ion‐Transporting Composite Membranes: III . Selectivity and Rate of Ion Transport in Nafion‐Impregnated Gore‐Tex Membranes Prepared by a High‐Temperature Solution Casting Method(1990)35 cited
• → Surface Modification by Electrostatic Self‐Assembly Followed by Covalent Fixation(2012)12 cited
• → Covalent and ionic species in cationic polymerizations: Rates of exchange(1988)8 cited
• → On the ionic and covalent characters of uranium-fluorine bonds in complex fluorides of uranium(1976)3 cited
• → O 2p Itinerant Electron Model for Magnetic Oxides(2021)