Preparation Characterization and Photocatalytic Activity of Polycrystalline ZnO/TiO2 Systems. 1. Surface and Bulk Characterization
Citations Over TimeTop 10% of 2001 papers
Abstract
Polycrystalline ZnO/TiO2 solids have been prepared with four different methods using home prepared TiO2 (anatase) or TiO2 (rutile) as supports and Zn(NO3)2·6H2O or Zn(CH3COO)2·2H2O as precursors for ZnO. The bulk and surface properties of the samples were investigated by means of TG-DTA, XRD, TEM, SEM-EDAX, XPS, BET surface area determination, and porosity measurements. XRD and TEM results indicate that no significant defect structures exist in any of the samples. The ZnO crystallinity and its enrichment on the surface of TiO2 particles were dependent on the preparation method. The surface areas generally decrease by increasing the amount of ZnO except when ZnO from Zn(CH3COO)2·2H2O was supported on TiO2 (rutile). The samples prepared from Zn(CH3COO)2·2H2O were more porous than those prepared from Zn(NO3)2·6H2O. This was confirmed by BET surface area determinations and SEM observations. XPS spectra indicate that the atomic ratio between OH- and O2- on the particles surface is similar for samples with the same ZnO content independent of the precursor used for the samples' preparation. Moreover a much higher segregation of ZnO was found for samples obtained by using the acetate precursor.
Related Papers
- → The role of the surface intermediates in the photoelectrochemical behaviour of anatase and rutile TiO2(1993)240 cited
- → Photodegradation of organic dyes based on anatase and rutile TiO2nanoparticles(2015)150 cited
- → Electrostatic potential calculations on crystalline TiO2: The surface reducibility of rutile and anatase(1983)33 cited
- → Infrared– active defects in a TiO2 mixture of coexisting anatase and rutile phases(2003)19 cited
- → 주형합성을 통한 메조포러스 TiO 2 제조 및 실리카 메조포어 내부에서의 TiO 2 상전이 거동 변화(2018)