Bimodal Size Distribution of Gold Nanoparticles under Picosecond Laser Pulses

Citations Over TimeTop 10% of 2005 papers

Abstract

The evolution of size distributions of gold nanoparticles under pulsed laser irradiation (Nd:YAG, lambda = 355 nm, pulse width 30 ps) was carefully observed by transmission electron microscopy. Interestingly, the initial monomodal size distribution of gold nanoparticles turned into a bimodal one, with two peaks in the number of particles, one at 6 nm and the other at 16-24 nm. The sizes for small particles depended very little on the irradiated laser energy. This change is attributed to laser-induced size reduction of the initial gold nanoparticles followed by the formation of small particles. In our analysis, we extracted a characteristic value for the size-reduction rate per one pulse and revealed that laser-induced size reduction of gold nanoparticles occurred even below the boiling point. When laser energy is insufficient for the boiling of particles, formation of gold vapor around liquid gold drops is thought to cause the phenomenon. With enough laser energy for the boiling, the formation of gold vapor around and inside liquid gold drops is responsible for the phenomenon. We also observed particles with gold strings after one pulse irradiation with a laser energy of 43 mJ cm(-2) pulse(-1), which is sufficient energy for the boiling. It is considered that such particles with gold strings are formed by the projection of gaseous gold from liquid gold drops with some volume of liquid gold around the bubble. On the basis of comparison with previous work, picosecond laser pulses are thought to be the most efficient way to cause laser-induced size reduction of gold nanoparticles.

Related Papers

• → Vaporization coefficients of SiO 2 and MgO(2017)15 cited
• → Experimental study and prediction of liquid nitrogen pool evaporation process on concrete surface(2020)4 cited
• → Vaporization of DMS Influenced by Foam(2015)2 cited
• → Study of vaporization of a single droplet impinging on a heated ceramic surface.(1987)2 cited
• → Vaporization of zinc oxide from defective spinel powders in vacuum.(1979)