Single-Component and Mixed Ferrocene-Terminated Alkyl Monolayers Covalently Bound to Si(111) Surfaces

Citations Over TimeTop 10% of 2006 papers

Abstract

Self-assembled ferrocene monolayers covalently bound to monocrystalline Si(111) surfaces have been prepared from the attachment of an amine-substituted ferrocene derivative to a pre-assembled acid-terminated alkyl monolayer using carbodiimide coupling. This derivatization strategy yielded nanometer-scale clean, densely packed monolayers, with the ferrocene units being more than 20 A from the semiconductor surface. The amount of immobilized electroactive units could be varied in the range 2 x 10(-11) to approximately 3.5 x 10(-10) mol cm(-2) by diluting the ferrocene-terminated chains by inert n-decyl chains. The highest coverage obtained for the single-component monolayer corresponded to 0.25-0.27 bound ferrocene per surface silicon atom. The electrochemical characteristics of the mixed n-decyl/ferrocene-terminated monolayers were found to not depend significantly on the surface coverage of ferrocene units. The reversible one-electron wave of the ferrocene/ferrocenium couple was observed at E degrees ' = 0.50 +/- 0.01 V vs SCE, and the rate constant of electron transfer kapp was about 50 s(-1).

Related Papers

• → Phase behavior and morphology of equimolar mixed cationic–anionic surfactant monolayers at the air/water interface: Isotherm and Brewster angle microscopy analysis(2008)24 cited
• → Mixed SAMs of backbone-functionalized tribenzotriquinacenes and alkanethiols: Synthesis, preparation and STM-investigations(2015)10 cited
• → Attachment of Alkyltrichlorosilanes to the Terminal 3,5-Dihydroxyphenyl Moiety of a Self-assembled Thiol Monolayer on Gold(2002)6 cited
• CYCLIC VOLTAMMETRY STUDY OF SELF-ASSEMBLED LAYER ON SILVER(2006)
• Formation process and topography characteristics of OTS self-assembled monolayers(2002)