Quasicubic α-Fe2O3 Nanoparticles with Excellent Catalytic Performance
Citations Over TimeTop 1% of 2006 papers
Abstract
Uniform quasicubic alpha-Fe(2)O(3) nanoparticles enclosed by six identical {110} planes were synthesized by a simple solvothermal method. TEM investigations revealed that they were formed through oriented attachment of primary nanocrystals assisted by Ostwald ripening, and PVP surfactant played an important role in control over the final morphology of the products. These quasicubic nanoparticles could catalyze oxidation of almost 100% CO at a temperature of 230 degrees C, much lower than those of nanophases with flowerlike, hollow, or other forms of irregular external morphologies having various crystal planes exposed to the gas, indicating that the external morphology and especially the exposure crystal planes of alpha-Fe(2)O(3) nanocatalyst affect the catalytic activity more significantly than the traditionally accepted factors (such as high BET surface area, hollow structure, etc.) do for CO catalytic oxidation.
Related Papers
- → Effects of activation conditions on BET specific surface area of activated carbon nanotubes(2004)68 cited
- → Preparation of Activated Carbon with Large Specific Surface Area from Reed Black Liquor(2007)40 cited
- → Superhigh Surface Area Determination of Microporous Carbons(1994)14 cited
- → Microwave-Alkali Activation on the Morphology and Structure of Bamboo Activated Carbon(2014)3 cited
- Calculation of BET surface area of microporous materials at different relative pressure(2006)