Synthesis and Characterization of Ultrahigh Crystalline TiO2 Nanotubes
Citations Over TimeTop 10% of 2006 papers
Abstract
Ultrahigh crystalline TiO2 nanotubes were synthesized by hydrogen peroxide treatment of very low crystalline titania nanotubes (TiNT-as prepared), which were prepared with synthesized TiO2 nanoparticles by hydrothermal methods in an aqueous NaOH solution. Thus, prepared ultrahigh crystalline TiO2 nanotubes (TiNT-H2O2) showed comparable crystallinity with high crystalline TiO2 nanoparticles. The details of nanotubular structures were elucidated by high resolution-transmission electron microscopy (HR-TEM), field emission-scanning electron microscopy (FE-SEM), energy-dispersive X-ray analysis in transmission electron microscopy (TEM-EDX), X-ray diffraction (XRD), photoluminescence (PL), and BET surface area. TiNT-H2O2 was found to be a multiwalled anatase phase only with an average outer diameter of approximately 8 nm and an inner diameter of approximately 5 nm and grown along the [001] direction to 500-700 nm long with an interlayer fringe distance of ca. 0.78 nm. The photocatalytic activity of TiNT-H2O2 was about 2-fold higher than those of TiNT-as prepared, synthesized TiO2 nanoparticles, and TiO2-P25 (Degussa) in the photocatalytic oxidation of trimethylamine gas under UV irradiation.
Related Papers
- → Photocatalytic CO2 Reduction with H2O on TiO2 Nanocrystals: Comparison of Anatase, Rutile, and Brookite Polymorphs and Exploration of Surface Chemistry(2012)849 cited
- → Bicrystalline TiO2 with controllable anatase–brookite phase content for enhanced CO2 photoreduction to fuels(2013)259 cited
- → Brookite versus anatase TiO2 photocatalysts: phase transformations and photocatalytic activities(2012)253 cited
- → Brookite and anatase nanomaterial polymorphs of TiO2 synthesized from TiCl3(2017)36 cited
- Raman and UV-Vis Absorption Studies on Nanosized TiO_2Particles(2000)