Influence of a TiCl4Post-Treatment on Nanocrystalline TiO2Films in Dye-Sensitized Solar Cells
Citations Over TimeTop 1% of 2006 papers
Abstract
In this study, the influence of the TiCl(4) post-treatment on nanocrystalline TiO(2) films as electrodes in dye-sensitized solar cells is investigated and compared to nontreated films. As a result of this post-treatment cell efficiencies are improved, due to higher photocurrents. On a microscopic scale TiO(2) particle growth on the order of 1 nm is observed. Despite a corresponding decrease of BET surface area, more dye is adsorbed onto the oxide surface. Although it seems trivial to match this finding with the improved photocurrent, this performance improvement cannot be attributed to higher dye adsorption only. This follows from comparison between incident photon to current conversion efficiency (IPCE) and light absorption characteristics. Since the charge transport properties of the TiO(2) films are already more than sufficient without treatment, the increase in short circuit current density J(SC) cannot be related to improvements in charge transport either. Transient photocurrent measurements indicate a shift in the conduction band edge of the TiO(2) upon TiCl(4) treatment. It is concluded that the main contribution to enhanced current originates from this shift in conduction band edge, resulting in improved charge injection into the TiO(2).
Related Papers
- → Factors Affect Dye Sensitized Solar Cells performance(2017)10 cited
- → Significant enhancement in the power conversion efficiency of porphyrin based dye sensitized solar cell by co-sensitization with metal free dye(2013)7 cited
- Susquehanna Chorale Spring Concert "Roots and Wings"(2017)
- Recent progress on tandem structured dye-sensitized solar cells(2012)
- → Investigation and optimization of dye-sensitized solar cells, under variable lighting conditions(2023)