Efficient CO Oxidation at Low Temperature on Au(111)

Citations Over TimeTop 10% of 2006 papers

Abstract

The rate of CO oxidation to CO2 depends strongly on the reaction temperature and characteristics of the oxygen overlayer on Au(111). The factors that contribute to the temperature dependence in the oxidation rate are (1) the residence time of CO on the surface, (2) the island size containing Au−O complexes, and (3) the local properties, including the degree of order of the oxygen layer. Three different types of oxygendefined as chemisorbed oxygen, a surface oxide, and a bulk oxideare identified and shown to have different reactivity. The relative populations of the various oxygen species depend on the preparation temperature and the oxygen coverage. The highest rate of CO oxidation was observed for an initial oxygen coverage of 0.5 monolayers that was deposited at 200 K where the density of chemisorbed oxygen is maximized. The rate decreases when two-dimensional islands of the surface oxide are populated and further decreases when three-dimensional bulk gold oxide forms. Our results are significant for designing catalytic processes that use Au for CO oxidation, because they suggest that the most efficient oxidation of CO occurs at low temperatureeven below room temperatureas long as oxygen could be adsorbed on the surface.

Related Papers

• → Overlayer thickness determination by XPS using the multiline approach(2008)57 cited
• → Elastic electron backscattering from overlayer/substrate systems(2001)18 cited
• Hydrophilic property of SiO2-TiO2 overlayer films and TiO2／SiO2 mixing films(2004)
• → Overlayer-induced resonant electronic states: A theoretical study(1992)3 cited
• → Second harmonic generation study of quantum well states in thin noble metal overlayer films(1997)1 cited