Surfactant-Assisted Route to Synthesize Well-Aligned ZnO Nanorod Arrays on Sol−Gel-Derived ZnO Thin Films
Citations Over TimeTop 10% of 2006 papers
Abstract
Anisotropic growth of ZnO nanorod arrays on ZnO thin films was achieved at a temperature of 90 degrees C by a surfactant-assisted soft chemical approach with control over size and orientation. ZnO thin films with c-axis preferred orientation had been achieved by the sol-gel technique. Lengths, diameters, and the degree of alignment of the ZnO nanorods were controlled by changing the experimental parameters. It was observed that the surfactant was essential to restrict the lateral growth of the nanorods, whereas the pH level of the reaction medium controlled the length of the nanorods. On the other hand, the orientation of the nanorods depended on the crystalline orientation of the film as well as the pH of the reaction medium. Room-temperature photoluminescence studies revealed that the ZnO nanorods with the best alignment exhibited the best emission property. The ZnO nanorods exhibited a strong UV emission peak at approximately 3.22 eV, ascribed to the band-edge emission. The field emission studies of the well-aligned nanorod arrays exhibited a low turn-on field of 1.7 V/microm to get an emission current density of 0.1 microA/cm(2).
Related Papers
- → Stability and Transformations of Heated Gold Nanorods(2011)30 cited
- → HPHT synthesis and magnetic property of -Fe2O3@C core-shell nanorods(2014)2 cited
- → Size-dependent water splitting activity of ZnO nanorods(2019)3 cited
- → Superfocusing effect in the chain of silver nanorods(2011)2 cited
- Solvothermal Synthesis of CdSxSe1-x Nanorods by Polymer Gel-Controlled Growth Strategy(2007)