Is the Band Gap of Pristine TiO₂ Narrowed by Anion- and Cation-Doping of Titanium Dioxide in Second-Generation Photocatalysts?

Citations Over TimeTop 1% of 2006 papers

Abstract

Second-generation TiO(2)-(x)D(x) photocatalysts doped with either anions (N, C, and S mostly) or cations have recently been shown to have their absorption edge red-shifted to lower energies (longer wavelengths), thus enhancing photonic efficiencies of photoassisted surface redox reactions. Some of the studies have proposed that this red-shift is caused by a narrowing of the band gap of pristine TiO(2) (e.g., anatase, E(bg) = 3.2 eV; absorption edge ca. 387 nm), while others have suggested the appearance of intragap localized states of the dopants. By contrast, a recent study by Kuznetsov and Serpone (J. Phys. Chem. B, in press) has proposed that the commonality in all these doped titanias rests with formation of oxygen vacancies and the advent of color centers (e.g., F, F(+), F(++), and Ti(3+)) that absorb the visible light radiation. This article reexamines the various claims and argues that the red-shift of the absorption edge is in fact due to formation of the color centers, and that while band gap narrowing is not an unknown occurrence in semiconductor physics it does necessitate heavy doping of the metal oxide semiconductor, thereby producing materials that may have completely different chemical compositions from that of TiO(2) with totally different band gap electronic structures.

Related Papers

• → OPTICAL PROPERTIES OF ANATASE TiO₂ UNDER THE HIGH PRESSURE(2001)5 cited
• → Structural, Electronic and Optical Properties of S-Doped Anatase TiO<sub>2</sub><sub></sub>(2015)3 cited
• → Doping Titanium Dioxide by Fluoride Ion(2019)2 cited
• → A study on the interaction of V2O5/TiO2 (anatase) by high-resolution electron microscopy (hrem)(1986)50 cited
• → GROWTH, SURFACE CHARACTERIZATION, AND REACTIVITY OF TIO2 ANATASE FILMS-EPSCOR(2004)