Highly Durable Proton Exchange Membranes for Low Temperature Fuel Cells
Citations Over TimeTop 10% of 2007 papers
Abstract
A novel method has been proposed to fabricate Nafion/poly(tetrafluoroethylene) (PTFE) composite proton exchange membranes (PEMs) with high durability and high chemical stability. In this method, Nafion ionomers were first converted into the Na(+) form, they were then fixed on PTFE frame micropores, and then the polymer was heat-treated at 270 degrees C. The chemical stability tests of the novel composite PEMs by Fenton's reagent demonstrate the significant improvement in the chemical durability. The Nafion/PTFE composite PEMs also show an excellent physical stability, and its RH-generated stress is 0.6 MPa at 25 RH% and 90 degrees C, substantially smaller than 3.1 MPa for pure Nafion membrane under the same conditions. In an in situ accelerating RH cyclic experiment, the degradation in the open circuit voltage (OCV) of the fuel cell assembled with the novel composite PEMs is 3.3 mV/h, significantly lower than 13.2 mV/h for a fuel cell assembled with the commercial Nafion membrane.
Related Papers
- → Effect of loading and distributions of Nafion ionomer in the catalyst layer for PEMFCs(2008)84 cited
- A Study on Electrochemical Characteristics of MEA with Nafion Ionomer Content in Catalyst Layer for PEMFC(2010)
- → Degradation Investigation of Nafion Ionomer Network In Catalyst Layers(2011)4 cited
- 고분자 전해질 막 연료전지의 촉매층 내의 나피온 아이오노머 양에 따른 단위 셀의 전기화학적 특성 연구(2010)
- Nafion Ionomer Content in Catalyst Layer for PEMFC Nafion Ionomer Content in Catalyst Layer for PEMFC(2010)