Tuning Magnetic Properties of α-MnO2 Nanotubes by K+ Doping
Citations Over TimeTop 12% of 2010 papers
Abstract
α-KxMnO2 nanotubes with x = 0.10, 0.12, 0.15, and 0.17 have been synthesized through acid and alkali treatments of the precursor α-MnO2 nanotubes. For the samples with x = 0.10 and 0.12, a large divergence of the ZFC and FC susceptibilities and pronounced hysteresis at low temperature are observed. However, the samples with x = 0.15 and 0.17 are antiferromagnetic with Néel temperatures of 25.4 and 25.3 K, respectively. The reciprocal susceptibility and electrical conductivity indicate that the samples with x = 0.15 and 0.17 undergo a charge separation transition from mixed/averaged valence state manganese ions to Mn3+ and Mn4+ between 250 and 300 K. Below half occupancy of the K+ site (x ≤ 0.125), the strong geometrical frustration due to the triangular lattice configuration and the mixture of Mn3+/Mn4+ result in the spin-glass behavior of the samples with x = 0.10 and 0.12. Above half occupancy of the K+ site, the samples with x = 0.15 and 0.17 exhibit an antiferromagnetic feature due to the charge separation of Mn3+ and Mn4+. Our experiments display that the magnetic properties of α-KxMnO2 can be tuned by varying the K+ content.
Related Papers
- Frustration and its effect on immersion in games : A developer viewpoint on the good and bad aspects of frustration(2015)
- On the Influence and Reason of Frustration on Study(2002)
- Frustration Education Upon College Students Should Be Strengthened(2002)
- On Young Students' Frustration Education(2003)
- Reflect on Carrying out Antifrustration Education Among the College Students(2004)