Structural and Thermochemical Chemisorption of CO2 on Li4+x(Si1–xAlx)O4 and Li4–x(Si1–xVx)O4 Solid Solutions
Citations Over TimeTop 10% of 2012 papers
Abstract
Different Li(4)SiO(4) solid solutions containing aluminum (Li(4+x)(Si(1-x)Al(x))O(4)) or vanadium (Li(4-x)(Si(1-x)V(x))O(4)) were prepared by solid state reactions. Samples were characterized by X-ray diffraction and solid state nuclear magnetic resonance. Then, samples were tested as CO(2) captors. Characterization results show that both, aluminum and vanadium ions, occupy silicon sites into the Li(4)SiO(4) lattice. Thus, the dissolution of aluminum is compensated by Li(1+) interstitials, while the dissolution of vanadium leads to lithium vacancies formation. Finally, the CO(2) capture evaluation shows that the aluminum presence into the Li(4)SiO(4) structure highly improves the CO(2) chemisorption, and on the contrary, vanadium addition inhibits it. The differences observed between the CO(2) chemisorption processes are mainly correlated to the different lithium secondary phases produced in each case and their corresponding diffusion properties.
Related Papers
- → Reduction of vanadium(V) to vanadium(IV) by NADPH, and vanadium(IV) to vanadium(III) by cysteine methyl ester in the presence of biologically relevant ligands(2007)23 cited
- → Theoretical investigation on coadsorption effect of O2 and H2O on Pt(111) surface(2015)10 cited
- → Speciation of Vanadium(IV) and Vanadium(V) Using Ion-exchange Chromatography and ICP-AES.(1994)11 cited
- → Effect of Ligands on the Iron(III)/Iron(II) System and Its Novel Application to the Simultaneous Flow Injection Determination of Vanadium(IV) and Vanadium(V)(1994)14 cited
- Vanadium Recovery from Vanadium-containing Leaching Solution with High Iron Concentration by Reducing Precipitating-Redissolving(2012)