Effect of Heat Treatment on the Lithium Ion Conduction of the LiBH4–LiI Solid Solution
Citations Over TimeTop 10% of 2013 papers
Abstract
The LiBH4–LiI solid solution is a good Li+ conductor and a promising crystalline electrolyte for all-solid-state lithium based batteries. The focus of the present work is on the effect of heat treatment on the Li+ conduction. Solid solutions with a LiI content of 6.25–50% were synthesized by high-energy ball milling and annealed at 140 °C. Powder X-ray diffraction and scanning electron microscopy were used for characterizing the samples and for comparing their crystallite sizes and the density of defects before and after the annealing. The Li+ conductivity was measured using impedance spectroscopy, resulting in conductivities exceeding 0.1 mS/cm at 30 °C and 10 mS/cm at 140 °C. It was found that the formation of defect-rich microstructures during ball milling increased the specific conductivities of these compounds significantly. The phase transition temperatures between the orthorhombic and hexagonal structures of LiBH4 were measured using differential scanning calorimetry (DSC). The measured transition temperatures range from 100 to −70 °C and show a linear decrease of 70 °C for every 10% of LiI addition up to a LiI content of 25%. The relative stability of the two structures was calculated using density functional theory, and together with the DSC measurements, the calculations were used to evaluate the change in entropic difference between the structures with LiI content.
Related Papers
- → Study of glass transition of metallic glasses by temperature-modulated differential scanning calorimetry (MDSC)(2000)10 cited
- → Differential Scanning Calorimetry (DSC)(2008)201 cited
- Microwave Synthesis and Characterization of Both Cubic and Orthorhombic ZrW_(0.8)Mo_(1.2)O_8(2004)
- → Implications of Global and Local Mobility in Amorphous Excipients as Determined by DSC and TM DSC(2009)
- → Synthesis and Crystal Structure of a New Orthorhombic Polytype of Potassium Ferricyanide(2022)