Optical and Vibrational Studies of Partially Edge-Terminated Vertically Aligned Nanocrystalline MoS2 Thin Films
Citations Over TimeTop 10% of 2013 papers
Abstract
We report the optical and vibrational properties of nanocrystalline MoS2 thin films, which are comprised of stripe-like partially edge-terminated vertically aligned (ETVA) nano-size crystals dispersed in ⟨001⟩ oriented regions, grown on large insulating substrates. From high-resolution transmission electron microscopy experiments, the average grain size of ETVA MoS2 layers was found to be ∼5 nm and consist of three to five monolayers. The ETVA and flat nanocrystalline regions were in equivalent proportions in the films. The films were highly transparent (∼80%), but the transmittance decreased as the energy of the incident light approached the band gap. Additionally, weak excitonic peaks were observed in both the absorption and transmission spectra. The room-temperature Raman study showed that the line shape for both E2g1 and A1g modes was significantly broader, and few additional Raman modes were observed in comparison to bulk MoS2. The broadening in the line shape of the A1g mode was analyzed using the phonon-confinement model, and the calculated grain size was in good agreement with transmission electron microscopy measurements. Moreover, the temperature coefficient of the A1g mode was determined from the temperature-dependent Raman studies.
Related Papers
- → Sliding wear behavior of nanocrystalline nickel coatings: Influence of grain size(2012)61 cited
- → Nanocrystalline 6061 Al Powder Fabricated by Cryogenic Milling and Consolidated via High Frequency Induction Heat Sintering(2014)6 cited
- → Room temperature creep behavior of nanocrystalline Gd2Zr2O7 ceramic with grain size below 10 nm(2020)3 cited
- Study of grain growth and spark plasma sintering of nanocrystalline Cu powder(2005)
- → Effect of annealing on tensile properties of electrodeposited nanocrystalline Ni with broad grain size distribution(2010)