Electrochemical Characterization of TiO2Blocking Layers for Dye-Sensitized Solar Cells
Citations Over TimeTop 10% of 2014 papers
Abstract
Thin compact layers of TiO2 are grown by thermal oxidation of Ti, by spray pyrolysis, by electrochemical deposition, and by atomic layer deposition. These layers are used in dye-sensitized solar cells to prevent recombination of electrons from the substrate (FTO or Ti) with the hole-conducting medium at this interface. The quality of blocking is evaluated electrochemically by methylviologen, ferro/ferricyanide, and spiro-OMeTAD as the model redox probes. Two types of pinholes in the blocking layers are classified, and their effective area is quantified. Frequency-independent Mott–Schottky plots are fitted from electrochemical impedance spectroscopy. Certain films of the thicknesses of several nanometers allow distinguishing the depletion layer formation both in the TiO2 film and in the FTO substrate underneath the titania film. The excellent blocking function of thermally oxidized Ti, electrodeposited film (60 nm), and atomic-layer-deposited films (>6 nm) is documented by the relative pinhole area of less than 1%. However, the blocking behavior of electrodeposited and atomic-layer-deposited films is strongly reduced upon calcination at 500 °C. The blocking function of spray-pyrolyzed films is less good but also less sensitive to calcination. The thermally oxidized Ti is well blocking and insensitive to calcination.
Related Papers
- → New insights regarding the calcination as a critical parameter in the synthesis of sol–gel made titania powders(2012)5 cited
- → Study on the Calcination Time of V2O5-WO3-MoO3/TiO2 Catalysts for SCR DeNOx(2018)4 cited
- → Effect of calcination conditions on MoO3/SiO2 catalysts for synthesis of methylphenyl carbonate(2002)5 cited
- → On the Crystals of CaO In Limestone Calcined at Different Temperatures(1957)1 cited
- The effect of calcination conditions on the photocatalytic performance of CaTiO_3(2007)