Mechanistic Characteristics of Metal-Assisted Chemical Etching in GaAs
Citations Over TimeTop 19% of 2014 papers
Abstract
Because of the unique physical properties, various GaAs micro- and nanostructures have attracted increasing research attention for many technical applications such as solar cells, light-emitting diodes, and field-effect transistors. In this regard, numerous fabrication techniques have been explored, and among all, metal-assisted chemical etching is successfully applied to GaAs in order to achieve cost-effective, large-scale, and complex structures. However, the detailed explanations as well as the corresponding etching mechanism have not been reported until now or simply relied on the hole injection model of Si in order to explain the phenomenon. In this work, we perform a more systematic study to further explore and assess the etching phenomenon of GaAs employing the Au catalyst and the [KMnO4/H2SO4] etch system. It is revealed that the anisotropic etching behavior of GaAs is predominantly due to the Au-induced surface defects at the Au/GaAs interface, which makes the particular area more prone to oxidation and thus results in the simple directional wet etching; for that reason, more anisotropic etch is obtained for the Au pattern with higher edge-to-surface-area ratio. All these findings not only offer additional insight into the MacEtch process of GaAs but also provide essential information on different etching parameters in manipulating this anisotropic wet etching to achieve the fabrication of complex GaAs structures for technological applications.
Related Papers
- → Improvement of Cr dry etching characteristics with the MERIE system(2000)2 cited
- → Evaluation of NLD mask dry etching system(1999)
- → Dry etching utilizing showered electron beam assisted etching(1992)
- Research on Dry-Etching Gratings and Wet-Etching Gratings(2003)
- → Electron cyclotron resonance-reactive CH/sub 4//H/sub 2//Ar with constant Ar flow for high etch rate and improvement of etched surface morphology(2004)