Role of Cu-Ion Doping in Cu-α-MnO2 Nanowire Electrocatalysts for the Oxygen Reduction Reaction
Citations Over TimeTop 10% of 2014 papers
Abstract
The role of Cu-ion doping in α-MnO2 electrocatalysts for the oxygen reduction reaction in alkaline electrolyte was investigated. Cu-doped α-MnO2 nanowires (Cu-α-MnO2) were prepared with varying amounts (up to ∼3%) of Cu2+ using a hydrothermal method. The electrocatalytic data indicate that Cu-α-MnO2 nanowires have up to 74% higher terminal current densities, 2.5 times enhanced kinetic rate constants, and 66% lower charge transfer resistances that trend with Cu content, exceeding values attained by α-MnO2 alone. The observed improvement in catalytic behavior correlates with an increase in Mn3+ content at the surface of the Cu-α-MnO2 nanowires. The Mn3+/Mn4+ couple is the mediator for the rate-limiting redox-driven O2/OH– exchange. O2 adsorbs via an axial site (the eg orbital on the Mn3+ d4 ion) at the surface or at edge defects of the nanowire, and the increase in covalent nature of the nanowire with Cu-ion doping leads to stabilization of O2 adsorbates and faster rates of reduction. A smaller crystallite size (roughly half) for Cu-α-MnO2 leading to a higher density of (catalytic) edge defect sites was also observed. This work is applicable to other manganese oxide electrocatalysts and shows for the first time there is a correlation for manganese oxides between electrocatalytic activity for the oxygen reduction reaction (ORR) in alkaline electrolyte and an increase in Mn3+ character at the surface of the oxide.
Related Papers
- → Study on manganese volatilization behavior of Fe–Mn–C–Al twinning-induced plasticity steel(2021)23 cited
- Effects of Manganese Availability on Acquisition and Distribution of Manganese,Iron and Phosphorus in Soybean [Glycine max (L.) Merr.](2010)
- Absorption of light in InP nanowire arrays(2014)
- → Studies in soil and plant manganese(1962)13 cited
- → The relative content of manganese in plants(1957)9 cited