Photoluminescence Quenching in Single-Layer MoS2 via Oxygen Plasma Treatment
Citations Over TimeTop 10% of 2014 papers
Abstract
By creating defects via oxygen plasma treatment, we demonstrate optical properties variation of single-layer MoS2. We found that, with increasing plasma exposure time, the photoluminescence (PL) evolves from very high intensity to complete quenching, accompanied by gradual reduction and broadening of MoS2 Raman modes, indicative of distortion of the MoS2 lattice after oxygen bombardment. X-ray photoelectron spectroscopy study shows the appearance of the Mo6+ peak, suggesting the creation of MoO3 disordered regions in the MoS2 flake. Finally, using band structure calculations, we demonstrate that the creation of MoO3 disordered domains upon exposure to oxygen plasma leads to a direct-to-indirect bandgap transition in single-layer MoS2, which explains the observed PL quenching.
Related Papers
- → La2MgTiO6:Bi3+/Mn4+ photoluminescence materials: Molten salt preparation, Bi3+ → Mn4+ energy transfer and thermostability(2020)21 cited
- → Photoluminescence of porous Si, oxidized then deoxidized chemically(1992)109 cited
- → Study of delocalized and localized states in ZnSeO layers with photoluminescence, micro-photoluminescence, and time-resolved photoluminescence(2019)7 cited
- → Excitons imaging in hybrid organic-inorganic films(2012)3 cited
- Photoluminescence excitation spectroscopy yields bandgap of Ga_5In_5P containing relatively ordered domains(1993)