Electromagnetic Field Absorbing Polypropylene Nanocomposites with Tuned Permittivity and Permeability by Nanoiron and Carbon Nanotubes
Citations Over TimeTop 10% of 2014 papers
Abstract
Highly efficient electromagnetic field absorption at gigahertz (GHz) was reported in the novel magnetic polymer nanocomposites (MPNCs) with in-situ synthesized Fe@Fe2O3 core@shell nanoparticles (NPs) or their decorated multiwall carbon nanotubes (MWNTs) dispersed in the polypropylene (PP) matrix through a one-pot bottom-up method. PP grafted maleic anhydride (PP-g-MA) with different molecular weights served as surfactant to stabilize the in-situ-formed NPs and simultaneously as compatibilizer to enhance the bonding at the PP–filler interfaces. Because of the strong magnetization of the PP MPNCs filled with 20.0 wt % Fe@Fe2O3 NPs stabilized by PP-g-MA (Mn = 800), a minimum reflection loss (RL) of −31.5 dB was observed at 18.0 GHz, and the frequency bandwidth with RL lower than −10.0 dB was 3.1 GHz (from 16.9 to 20.0 GHz) in the MPNC sample with a thickness of 5.5 mm. However, due to the lack of magnetic loss, only a weak RL of 4.3 dB was found at frequency of 16.8 GHz for the PP/PP-g-MA (Mn = 800)/1.0 wt % MWNTs nanocomposites sample with a thickness of 5.5 mm. When the PP MPNCs filled with Fe@Fe2O3 NPs decorated MWNTs (sample thickness of 5.0 mm) in the presence of low molecular weight PP-g-MA (Mn = 800), the RL of −24.5 dB at 20.0 GHz was observed. Through simply changing Mn of PP-g-MA from 800 to 8000, more oxidized iron resulted in a decreased permeability and smaller RL in the high frequency range. The in-situ-formed nanofillers significantly reduced the flammability of PP for potential wide applications.
Related Papers
- → Handbook of Polypropylene and Polypropylene Composites(1999)331 cited
- Structure and property of Cu-based thermosensitive nanocomposite(2006)
- Modification and characterization of polypropylene(2014)
- → Bulk Metal and Ceramics Nanocomposites(2003)42 cited
- → Oxygen absorption studies on polypropylene(1964)1 cited