Visible-Light-Induced Photocatalytic Activity in FeNbO₄ Nanoparticles

Citations Over TimeTop 13% of 2008 papers

Abstract

A novel method was used to synthesize orthorhombic FeNbO4 nanoparticles by a hydrothermal process followed by calcination at 600 °C, and their optical, photoelectrochemical, and photocatalytic properties were investigated. The microstructural and local structural properties were characterized using X-ray diffraction, field-emission scanning electron microscopy, transmission electron microscopy (TEM), and Raman spectroscopy. The FeNbO4 particles obtained were composed of much smaller nanocrystallines, with an average size of 10−20 nm, compared to particles prepared at 1000 °C through a conventional solid-state reaction method. Moreover, the optical band gap energy of the nanoparticles was estimated to be 1.93 eV from the UV−vis diffuse reflectance, and their flat-band potential in 1 M NaOH was −0.4 V (SCE). The X-ray photoelectron spectroscopy analysis revealed that the nanoparticles had fewer surface defects, such as oxygen vacancies, than the particles prepared by the solid-state reaction method. The FeNbO4 nanoparticles also exhibited a much higher photocatalytic activity for the degradation of rhodamine B dye solution under visible light irradiation (>420 nm). This higher photocatalytic activity of the FeNbO4 nanoparticles was attributed to their higher optical absorption ability and smaller particle size, as well as fewer surface defects.

Related Papers

• → Second derivative diffuse reflectance spectroscopy for estimating tissue hypoxia(2021)12 cited
• → A Brief Look at Optical Diffuse Reflection (ODR) Spectroscopy(2023)5 cited
• → Sampling depth in infrared diffuse reflection spectroscopy of undiluted samples(1988)9 cited
• → <title>Fiber-remote reflectance spectroscopy with an optimized diffuse reflectance sensor system</title>(1995)2 cited
• → Evaluation of the Scar Treatment using Near Infrared Diffuse Reflectance Spectroscopy(2016)