Sb2S3-Sensitized Nanoporous TiO2 Solar Cells
The Journal of Physical Chemistry C2009Vol. 113(11), pp. 4254–4256
Citations Over TimeTop 1% of 2009 papers
Abstract
Extremely Thin Absorber (ETA) solar cells were made using chemical-bath-deposited Sb2S3 as the absorber and TiO2/CuSCN as the interpenetrating electron/hole conductors. A solar conversion efficiency of 3.37% at 1 sun illumination was obtained. Surface oxidation of the Sb2S3 formed a passivation layer on Sb2S3: without this oxidation, much poorer cells were obtained. Preliminary stability measurements showed good stability over 3 days of illumination (at 60 mW/cm2) under load.
Related Papers
- → Passivation and Surface Film Formation(1996)7 cited
- → Elimination of parasitic effects in floating junction rear surface passivation for solar cells(1996)17 cited
- → Sulfur passivation of 3C-SiC thin film(2018)4 cited
- Development of High Performance Chromium-Free Passivation Agent Suitable for Coating of Aluminum Alloy and Optimization of Passivation Technology(2012)
- Passivation method of 317L stainless steel used in medicine(2002)