Fast Energy Migration in Pyronine-Loaded Zeolite L Microcrystals

Citations Over TimeTop 10% of 1999 papers

Abstract

The stacking of pyronine and oxonine in the channels of zeolite L microcrystals is possibly due to their high affinity for entering the channels and to the narrowness of inside the channels, which prevents the dyes from gliding past each other. This allowed us to invent experiments for observing energy migration in pyronine-loaded zeolite L microcrystals of cylinder morphology. Organic dyes have the tendency to form aggregates at relatively low concentrations which cause fast thermal relaxation of electronic excitation energy. The role of the zeolite is to prevent this aggregation even at very high concentrations and to superimpose a specific organization. Light is absorbed by a pyronine molecule located somewhere in one of the zeolite channels. The excitation energy migrates preferentially in both directions along the axis of the cylinder because of the pronounced anisotropy of the system. It is eventually trapped by an oxonine located at the front or at the back of the microcrystal. This process is called front−back trapping. The electronically excited oxonine then emits the excitation with a quantum yield of approximately one. The pronounced anisotropy of the electronic transition moments of both pyronine and oxonine can be observed in an optical fluorescence microscope by means of a polarizer. Maximum luminescence appears parallel to the longitudinal axis of the cylindrical microcrystals, extinction appears perpendicular to it, and their base always appears dark. We report experimental results for the front−back trapping efficiency of pyronine-loaded zeolite L microcrystals of different average lengths, namely 700, 1100, and 1500 nm, different pyronine occupation probability, ranging from 0.03 to 0.48; and modification at the base with oxonine as luminescent traps. Extremely fast electronic excitation energy migration along the axis of cylindrical crystals has been observed, supported by the increase of the effective excitation lifetime caused by self-absorption and re-emission of the pyronine vertical to the cylinder axis. Effective energy migration lengths of up to 166 nm upon pyronine excitation have been observed, which thus leads to the remarkable properties of this material.

Related Papers

• → Optimum polarizer combinations for twisted nematic displays(1977)5 cited
• Polysulfone으로 제올라이트 A를 고정화한 방사성 물질제거용 PS-zeolite 비드 제조(2015)
• A Verification by Experiments about Ammonia' influences to Polarizers(2009)
• A Course of Polarizer Knowledge Part Four The Structure and Manufacture of Polarizer(2012)
• 쳔연 Zeolite ( 제올라이트 ) 를 이용한 중금속 흡착제의 개발(1991)