Tuning Cell Adhesion on Gradient Poly(2-hydroxyethyl methacrylate)-Grafted Surfaces

Citations Over TimeTop 10% of 2005 papers

Abstract

A simple yet versatile method was developed to prepare a low-density polymerization initiator gradient, which was combined with surface-initiated atom transfer radical polymerization (ATRP) to produce a well-defined poly(2-hydroxyethyl methacrylate) (HEMA) gradient substrate. A smooth variation in film thickness was measured across the gradient, ranging from 20 A to over 80 A, but we observed a nonmonotonic variation in water contact angle. Fits of X-ray reflectivity profiles suggested that at the low graft density end, the polymer chain structure was in a "mushroom" regime, while the polymer chains at high graft density were in a "brush" regime. It was found that the "mushroom" region of the gradient could be made adhesive to cells by adsorbing adhesion proteins, and cell adhesion could be tuned by controlling the density of the polymer grafts. Fibroblasts were seeded on gradients precoated with fibronectin to test cellular responses to this novel substrate, but it was found that cell adhesion did not follow the expected trend; instead, saturated cell adhesion and spreading was found at the low grafting density region.

Related Papers

• → Surface functionalization of nanodiamond particles via atom transfer radical polymerization(2006)126 cited
• → Uniform PEO Star Polymers Synthesized in Water via Free Radical Polymerization or Atom Transfer Radical Polymerization(2010)27 cited
• → Polystyrene/clay nanocomposites by atom transfer radical nitroxide coupling chemistry(2012)18 cited
• → Synthesis and characterization of poly(2-ethylhexyl acrylate) prepared via atom transfer radical polymerization, reverse atom transfer radical polymerization and radical polymerization(2013)12 cited
• Synthesis of Polymer Brushes from Flat Surface——Research Progress of Surface-initiated Atom Transfer Radical Polymerization(2006)