Temperature-Controlled Flow Switching in Nanocapillary Array Membranes Mediated by Poly(N-isopropylacrylamide) Polymer Brushes Grafted by Atom Transfer Radical Polymerization

Citations Over TimeTop 10% of 2006 papers

Abstract

We report actively controlled transport that is thermally switchable and size-selective in a nanocapillary array membrane (NCAM) prepared by grafting poly(N-isopropylacrylamide) (PNIPAAm) brushes onto the exterior surface of a Au-coated polycarbonate track-etched membrane. A smooth Au layer on the membrane surface, which is key to obtaining a uniform polymer film, was prepared by thermal evaporation of approximately 50 nm Au on both exterior surfaces. After evaporation, the inner diameter of the pore is reduced slightly, but the NCAM retains a narrow pore size distribution. PNIPPAm brushes with 10-30 nm (dry film) thickness were grafted onto the Au surface through surface-initiated atom transfer radical polymerization (ATRP) using a disulfide initiator, (BrC(CH3)2COO(CH2)11S)2. Molecular transport through the PNIPAAm polymer brush-modified NCAMs was investigated by real-time fluorescence measurements using fluorescein isothiocyanate (FITC)-labeled dextrans ranging from 4.4 to 282 kDa in membranes with variable initial pore diameters (80, 100, and 200 nm) and different PNIPAAm thicknesses. Manipulating the temperature of the NCAM through the PNIPAAm lower critical solution temperature (LCST) causes large, size-dependent changes in the transport rates. Over specific ranges of probe size, transport is completely blocked below the LCST but strongly allowed above the LCST. The combination of the highly uniform PNIPAAm brush and the monodisperse pore size distribution is critical in producing highly reproducible switching behavior. Furthermore, the reversible nature of the switching raises the possibility of using them as actively controlled filtration devices.

Related Papers

• → Temperature controlled surface hydrophobicity and interaction forces induced by poly (N-isopropylacrylamide)(2009)83 cited
• → Thermo-responsive release from interpenetrating porous silica–poly(N-isopropylacrylamide) hybrid gels(2001)46 cited
• → Development of highly thermoresponsive fluorescent sensors consisting of plasmonic silver nanoprisms and poly(N-isopropylacrylamide)–fluorophore composites(2015)6 cited
• Synthesis and Thermosensitive Characterization of DTPA-Poly(N-isopropylacrylamide)(2007)
• Controllable release of ibuprofen from thermo-sensitive poly(N-isopropylacrylamide) hydrogel(2011)