Rheological Studies of Thermosensitive Triblock Copolymer Hydrogels
Citations Over TimeTop 11% of 2006 papers
Abstract
Hydrogel formation by physical cross-linking is a developing area of research toward materials suitable for pharmaceutical and biomedical applications. Polymers exhibiting lower critical solution temperature (LCST) behavior in aqueous solution are used in this study to prepare hydrogels. Four triblock copolymers (ABA) with thermosensitive poly(N-(2-hydroxypropyl) methacrylamide lactate) A-blocks and a hydrophilic poly(ethylene glycol) B-block have been synthesized. The molecular weight of the hydrophilic PEG block was fixed at 10 kDa, whereas the molecular weight of the pHPMAm-lactate block was varied between 10 and 20 kDa. The rheological characteristics of these polymer hydrogels were studied as a function of temperature, concentration, and the length of the thermosensitive blocks. Gelation occurred rapidly upon increasing the temperature to 37 degrees C, which makes this system suitable as an injectable formulation. The gels became stronger with increasing temperature and concentration, and moreover they behaved as critical gels, which means that G' and G' ' follow power laws over the entire frequency range. Surprisingly, with increasing length of the thermosensitive blocks, weaker hydrogels were formed. This trend can be explained by the cross-link density of the physical network, which increases with decreasing length of the thermosensitive blocks.
Related Papers
- → Preparation and characterization of guanidinated N-3-aminopropyl methacrylamide-N-2-hydroxypropyl methacrylamide copolymers as gene delivery carriers(2011)9 cited
- → Helicity Induction in N-[(4-Butyl)triphenylmethyl]methacrylamide Sequence via Radical Copolymerization with Chiral Monomers(2006)5 cited
- → Formulation and synthesis of hydrogels having lower critical solution temperature near body temperature(2017)1 cited
- → Polymerization and Characterization of N-[o-(4-phenyl-4,5-dihydro-1,3-oxazol-2-yl)phenyl] Methacrylamide(2014)
- TEMPERATURE RESPONSIVE METHACRYLAMIDE POLYMERS WITH ANTIBACTERIAL ACTIVITY(2010)