Study on the Anatase to Rutile Phase Transformation and Controlled Synthesis of Rutile Nanocrystals with the Assistance of Ionic Liquid
Citations Over TimeTop 10% of 2010 papers
Abstract
We developed a route to synthesize rutile TiO(2) nanocrystals (NCs) with the assistance of 1-butyl-3-methylimidazolium chloride (bmim(+)Cl(-)). The phase transformation from anatase to rutile phase was investigated, and a simple model to describe the phase transformation process was proposed considering that the nucleation and growth of rutile phase were determined by the aggregation manner of anatase NCs and Ostwald ripening process, respectively. It was demonstrated that the surfactant-like nature of the IL used was crucial for controlling the crystallization process via controlling the aggregation manner of the NCs. The phase, shape, and size of TiO(2) NCs could be tuned by the controlling the operating conditions, such as temperature, solution acidity, and reactant concentration of the bmim(+)Cl(-)/TiCl(4)/H(2)O reaction system. Phase-pure rutile multipods and 1D nanorods with different sizes were controllably obtained.
Related Papers
- → The role of the surface intermediates in the photoelectrochemical behaviour of anatase and rutile TiO2(1993)240 cited
- → Synthesis of Single-Crystalline Anatase TiO2 Nanorods With High-Performance Dye-Sensitized Solar Cells(2014)36 cited
- → Electrostatic potential calculations on crystalline TiO2: The surface reducibility of rutile and anatase(1983)33 cited
- → Infrared– active defects in a TiO2 mixture of coexisting anatase and rutile phases(2003)19 cited
- → 주형합성을 통한 메조포러스 TiO 2 제조 및 실리카 메조포어 내부에서의 TiO 2 상전이 거동 변화(2018)