Molecular Architecture: Construction of Self-Assembled Organophosphonate Duplexes and Their Electrochemical Characterization

Citations Over TimeTop 11% of 2012 papers

Abstract

Self-assembled monolayers of phosphonates (SAMPs) of 11-hydroxyundecylphosphonic acid, 2,6-diphosphonoanthracene, 9,10-diphenyl-2,6-diphosphonoanthracene, and 10,10'-diphosphono-9,9'-bianthracene and a novel self-assembled organophosphonate duplex ensemble were synthesized on nanometer-thick SiO(2)-coated, highly doped silicon electrodes. The duplex ensemble was synthesized by first treating the SAMP prepared from an aromatic diphosphonic acid to form a titanium complex-terminated one; this was followed by addition of a second equivalent of the aromatic diphosphonic acid. SAMP homogeneity, roughness, and thickness were evaluated by AFM; SAMP film thickness and the structural contributions of each unit in the duplex were measured by X-ray reflection (XRR). The duplex was compared with the aliphatic and aromatic monolayer SAMPs to determine the effect of stacking on electrochemical properties; these were measured by impedance spectroscopy using aqueous electrolytes in the frequency range 20 Hz to 100 kHz, and data were analyzed using resistance-capacitance network based equivalent circuits. For the 11-hydroxyundecylphosphonate SAMP, C(SAMP) = 2.6 ± 0.2 μF/cm(2), consistent with its measured layer thickness (ca. 1.1 nm). For the anthracene-based SAMPs, C(SAMP) = 6-10 μF/cm(2), which is attributed primarily to a higher effective dielectric constant for the aromatic moieties (ε = 5-10) compared to the aliphatic one; impedance spectroscopy measured the additional capacitance of the second aromatic monolayer in the duplex (2ndSAMP) to be C(Ti/2ndSAMP) = 6.8 ± 0.7 μF/cm(2), in series with the first.

Related Papers

• → Thin film and surface characterization by specular X-ray reflectivity(1997)250 cited
• → Stabilization of Langmuir monolayer of hydrophobic thiocholesterol molecules(2008)8 cited
• → INVESTIGATION OF SOL-GEL GROWN ZnO THIN FILM: WAVELET ANALYSIS AND SIMULATED ANNEALING OPTIMIZED X-RAY REFLECTIVITY(2012)4 cited
• X-Ray Reflectivity for the characterisation of thin films(2004)
• → Non-destructive characterization of thin silicides using X-ray reflectivity(2002)