Toward Design of Magnetic Nanoparticle Clusters Stabilized by Biocompatible Diblock Copolymers for T2-Weighted MRI Contrast
Citations Over TimeTop 10% of 2014 papers
Abstract
We report the fabrication of magnetic particles comprised of clusters of iron oxide nanoparticles, 7.4 nm mean diameter, stabilized by a biocompatible, amphiphilic diblock copolymer, poly(ethylene oxide-b-D,L-lactide). Particles with quantitative incorporation of up to 40 wt % iron oxide and hydrodynamic sizes in the range of 80-170 nm were prepared. The particles consist of hydrophobically modified iron oxide nanoparticles within the core-forming polylactide block with the poly(ethylene oxide) forming a corona to afford aqueous dispersibility. The transverse relaxivities (r2) increased with average particle size and exceeded 200 s(-1) mM Fe(-1) at 1.4 T and 37 °C for iron oxide loadings above 30 wt %. These experimental relaxivities typically agreed to within 15% with the values predicted using analytical models of transverse relaxivity and cluster (particle core) size distributions derived from cryo-TEM measurements. Our results show that the theoretical models can be used for the rational design of biocompatible MRI contrast agents with tailored compositions and size distributions.
Related Papers
- → Synthesis of copolymers. I. Copolymers of styrene and of α‐methylstyrene(1972)12 cited
- → Anionic copolymerization of α,ω-dihydroxyoligodimethylsiloxane with organocyclosiloxanes(2008)2 cited
- STUDY ON COPOLYMERIZATION OF D_3~F, D_4(2002)
- Copolymerization of N-vinylformamid and N-vinylcaprolactam(2006)
- → [Research advances on the application of biocompatible materials in treating diabetic wounds].(2021)