Adhesion and Friction Properties of Polymer Brushes: Fluoro versus Nonfluoro Polymer Brushes at Varying Thickness

Citations Over TimeTop 10% of 2014 papers

Abstract

A series of different thicknesses of fluoro poly(2,2,2-trifluoroethyl methacrylate) and its analogous nonfluoro poly(ethyl methacrylate) polymer brushes were prepared via surface-initiated ATRP (SI-ATRP) on Si(111) surfaces. The thiol-yne click reaction was used to immobilize the SI-ATRP initiator with a high surface coverage, in order to achieve denser polymer brushes (grafting density from ~0.1 to 0.8 chains/nm(2)). All polymer brushes were characterized by static water contact angle measurements, infrared absorption reflection spectroscopy, and X-ray photoelectron spectroscopy. Adhesion and friction force measurements were conducted with silica colloidal probe atomic force microscopy (CP-AFM) under ambient and dry (argon) conditions. The fluoro poly(2,2,2-trifluoroethyl methacrylate) polymer showed a decrease in adhesion and friction with increasing thickness. The analogous nonfluoro poly(ethyl methacrylate) polymer brushes showed high adhesion and friction under ambient conditions. Friction coefficients down to 0.0057 (ambient conditions) and 0.0031 (dry argon) were obtained for poly(2,2,2-trifluoroethyl methacrylate) polymer brushes with 140 nm thickness, which are the lowest among these types of polymer brushes.

Related Papers

• → Surface functionalization of nanodiamond particles via atom transfer radical polymerization(2006)126 cited
• → Universal Strategy for Efficient Fabrication of Blood Compatible Surfaces via Polydopamine-Assisted Surface-Initiated Activators Regenerated by Electron Transfer Atom-Transfer Radical Polymerization of Zwitterions(2020)89 cited
• → A Facile Route to Poly(acrylic acid) Brushes Using Atom Transfer Radical Polymerization(2005)117 cited
• → Synthesis and properties of cross-linkable block copolymer end-capped with 2, 2, 3, 4, 4, 4-hexafluorobutyl methacrylate(2011)9 cited
• → Polymer Brushes by Atom Transfer Radical Polymerization(2004)19 cited