Facile Method to Prepare Smooth and Homogeneous Polymer Brush Surfaces of Varied Brush Thickness and Grafting Density

Citations Over TimeTop 12% of 2009 papers

Abstract

This Article describes a facile method to prepare smooth and homogeneous polymer brush surfaces of variable grafting density from a solid surface by combining Langmuir-Blodgett (LB) deposition with surface-initiated atom transfer radical polymerization (SI-ATRP). This method is successfully demonstrated by the preparation of thermoresponsive poly(N-isopropylacrylamide) (PNIPAM) brush surfaces on smooth silicon and quartz substrates. With the custom-synthesized inert diluent whose chemical structure, except end-functionality, is the same as that of the reactive initiator, smooth and chemically homogeneous mixed monolayers of initiators and inert diluents are immobilized on a solid surface by LB deposition, allowing the further variation of the grafting density of PNIPAM brushes grafted from the initiator monolayers of varied initiator coverage. With the optimized molar ratio of deactivator, Cu(II) in the Cu(I)-ligand catalyst complex, the brush thickness of PNIPAM brushes at varied grafting density is controlled to grow nearly linearly with reaction time while smoothness and chemical homogeneity of PNIPAM brushes are achieved. For the demonstrated PNIPAM brush surfaces, the thermoresponsive characteristics of PNIPAM brushes are also verified. This combined LB-ATRP method can be applied to graft a variety of polymer brushes, including polyelectrolytes and block copolymers, from different solid substrates.

Related Papers

• → A switchable polymer brush system for antifouling and controlled detection(2017)36 cited
• → Excluded volume effects in compressed polymer brushes: A density functional theory(2015)21 cited
• → A switchable polymer layer: Chain folding in end-charged polymer brushes(2001)11 cited
• → Compression of Polymer Brushes Under a Lateral Force(2004)9 cited
• → Sliding Friction between Polymer-brush-bearing Surfaces: Crossover from Brush-brush Interfacial Shear to Polymer-substrate Slip.(2000)