Double Phase Separation Induced by Polymerization in Ternary Blends of Epoxies with Polystyrene and Poly(methyl methacrylate)

Citations Over TimeTop 10% of 2001 papers

Abstract

Ternary blends based on a stoichiometric mixture of diglycidyl ether of bisphenol A (DGEBA) and 4,4‘-diaminodiphenyl sulfone (DDS), monodisperse polystyrene (PS, 8.3 × 104 g/mol), and monodisperse poly(methyl methacrylate) (PMMA, 8.86 × 104 g/mol) were polymerized at constant temperature. Blends containing a total amount of 8 wt % of both thermoplastics (with different PS/PMMA ratios), were initially homogeneous at 135 °C. When they were polymerized at this temperature, a double phase separation was clearly observed by light transmission. At conversions close to 0.08, the system became opalescent due to the generation of a PS-rich phase; at conversions close to 0.27, a new phase separation process took place, generating a PMMA-rich phase. TEM (transmission electron microscopy) observations confirmed the existence of three different phases: the epoxy matrix, PS-rich particles with a broad size distribution, and PMMA-rich particles. Some of the PS particles appeared encapsulated by the PMMA-rich phase (core−shell particles). The double phase separation process was analyzed using a Flory−Huggins model. Experimental results could be explained by following the evolution of phase diagrams with conversion. The initial composition was located in the region of homogeneous solutions. As conversion increased, the system entered the equilibrium region between two phases (first phase separation process), and at higher conversions it attained the region where three phases coexist at equilibrium (second phase separation process). Depending on the PS/PMMA ratio, the model predicted the possibility of a phase inversion following the first phase separation process. This was also inferred from measurements of the evolution of the complex viscosity during polymerization.

Related Papers

• → Phase behavior of poly(3-alkylthiophene)/polystyrene blends(2009)28 cited
• → UCST behaviour for high-molecular-weight polymer blends and estimation of segmental χ parameters from their miscibility(1996)17 cited
• → Immiscibility with upper-critical solution temperature phase diagrams for poly(methyl methacrylate)/polyesters blends(2007)13 cited
• → Effect of Pressure on the Miscibility of Polyethylene/Poly(ethylene‐alt‐propylene) Blends(2006)6 cited
• → Immiscibility, upper critical solution temperature, and miscibility in blends of poly(vinyl ether)s with polyacrylics: Effects of pendant groups(2007)6 cited