Rheology and Molecular Weight Distribution of Hyperbranched Polymers

Citations Over TimeTop 10% of 2002 papers

Abstract

We study the melt rheology and molecular weight distribution of four short chain branched hyperbranched polyesters with different molecular weights and containing branched monomers of various alkyl chain lengths n (2 → 4; n is the number of CH2 groups in the alkyl chain). We find that the molecular weight distribution for all our samples obeys the static scaling form n(M) ∼ M- τexp(−M/Mchar) where n(M) is the number density of hyperbranched polymers with mass M, Mchar is the largest characteristic molecular weight, and τ is the polydispersity exponent. The values of τ for all our samples (either 1.35 or 1.55) are close to but not the same as the mean field value of τ = 1.5, a consequence of the fact that our polymers were synthesized under non-mean-field polycondensation conditions. For all our samples, we found that the rheology at low and intermediate frequencies could be modeled accurately using a dynamic scaling theory based on the Rouse model. This confirms that these hyperbranched polymers behave as polymeric fractals which are essentially unentangled. For these polymers, the fractal dimension in the melt was found to be consistent with the hyperscaling relation for hyperbranched polymers df = 3, although we found rheology to be rather insensitive to df for our system.

Related Papers

• → Preparation and extensive characterization of hyaluronan with narrow molecular weight distribution(2016)47 cited
• → Kinetic analysis of AB2 polycondensation in the presence of multifunctional cores with various reactivities(2012)17 cited
• → A segregation approach to molecular weight control in controlled degradation of polymers(2002)1 cited
• → High-Temperature Gel Permeation Chromatography: Improvement in the Dispersity Characterization of Molecular Weight Distributions of Polyolefins(1982)7 cited
• → The effect of the polydispersity of the reactants, of monofunctional molecules and of cyclization, on the molecular weight distribution of linear polymers in non-equilibrium polycondensation and polyaddition reactions(1979)2 cited