Role of Architecture on the Conformation, Rheology, and Orientation Behavior of Linear, Star, and Hyperbranched Polymer Melts. 1. Synthesis and Molecular Characterization

Citations Over TimeTop 13% of 2002 papers

Abstract

Polymer architecture plays an important role in the solution, rheological, mechanical and processing behavior. In this series of two papers, we explore the role of branching, especially branch density, on the conformation and rheology of homopolymers. A series of model star-core hyperbranched polystyrenes (HBPS) with branch functionality, f, ranging from approximately 15 to 55, and branch molecular weight Mbr of 5, 10, 20, and 50 kg/mol are synthesized and characterized via triple detection SEC3 for the molecular weight, polydispersity, intrinsic viscosity, and radius of gyration. Compared to linear polymers and symmetric stars with three and eight arms of the same total molecular weight, these polymers exhibit considerably lower radius of gyration, Mark−Houwink exponent, and intrinsic viscosity. The hydrodynamic radii of HBPS with the highest branch density (f ≈ 50) are only about half the corresponding values of linear polymers of the same molecular weight, whereas this ratio is equal to 0.8 for symmetric stars. Our measurements suggest that HBPS have a very compact shape, high segmental density, and a starlike architecture. HBPS with branches shorter than the characteristic critical molecular weight exhibit a linear dependence of zero-shear viscosity on molecular weight, suggesting a lack of entanglements, and further indicating the starlike nature of the HBPS. Study of the rheology and flow birefringence of model polystyrenes will be presented in the following publication in this journal (Macromolecules 2003, 36, 407).

Related Papers

• → Chain Conformation of Water-Insoluble Hyperbranched Polysaccharide from Fungus(2007)132 cited
• → Hydrodynamic radius of polyethylene glycol in solution obtained by dynamic light scattering(2010)106 cited
• → Experimental and theoretical studies of scaling of sizes and intrinsic viscosity of hyperbranched chains in good solvents(2013)39 cited
• → Mean square radius of gyration and hydrodynamic radius of jointed star (dumbbell) and H‐comb polymers(1996)11 cited
• Radius of gyration and intrinsic viscosity of polyelectrolyte solutions(1993)